Sikafloor®-217
Sikafloor®-217 is a 100 % solids, low VOC, low odour, water-clear, aesthetic, high gloss epoxy resin used to create premium quality high build coatings, broadcast or trowel-applied surfacings such as Sikafloor® Quartzite®, DecoFlake®.
Protective coatings.
Local knowledge.
KNOW THE
SURFACE.
PLAN THE
COATING.
Sikafloor®-217 is a 100 % solids, low VOC, low odour, water-clear, aesthetic, high gloss epoxy resin used to create premium quality high build coatings, broadcast or trowel-applied surfacings such as Sikafloor® Quartzite®, DecoFlake®.
Start with the surface, the existing finish and the way the space or equipment is used. Our team can help you work through product choices and the requirements for your project.
Get into the details
The surface.
Identify the material, its condition and the work you’re planning.
The system.
Confirm product suitability, preparation and compatibility with our team.
The conditions.
Check the current manufacturer instructions for application, installation or maintenance requirements.
THE DETAILS.
ALL HERE.
Keep the technical information close.
Use the current manufacturer documents when planning the work.
| Packaging | A+B = 10 L (2.64 US gal) Unit Component A: 6.67 L (1.76 US gal) Component B: 3.33 L (0.88 US gal) |
|---|---|
| ENVIRONMENTAL INFORMATION | Conformity with LEED® v4 MRc 2 (Option 1): Building Product Disclosure and Optimization – Environmental Product Declarations. Conformity with LEED® v4 EQc 2: Low-Emitting Materials. |
| APPROVALS / CERTIFICATES | Meets CFIA requirements for use in food plants. |
| Shelf Life | 2 years when stored in original, unopened packaging. |
| Storage Conditions | Store dry at temperatures between 5 °C to 32 °C (41 °F to 89 °F). Protect from freezing. If frozen, contact Sika Canada. |
| Volatile organic compound (VOC) content | ~56 g/L |
| Viscosity | A+B: ~500 cPs |
| Solid content by volume | ~100 % |
| Shore D Hardness | ~80 (ASTM D2240) |
| Abrasion Resistance | ~0,076 g loss: CS-17 wheel /1000 g /1000 cycles- (ASTM D4060) |
| Compressive Strength | ~49.9 MPa (~7250 psi) (ASTM C579) |
| Tensile Strength | ~39.5 MPa (~5728 psi) (ASTM D638) |
| Pull-Off Strength | > 2.5 MPa (> 363 psi) concrete failure (ASTM D7234) |
| Chemical Resistance | Consult Sika Canada |
| Coefficient of Friction | ~0.32 Wet (smooth coating) ~0.92 Dry (smooth coating) ANSI A326.3 (DCOF - BOT 3000e) |
| Water Absorption | ~0.13 % (2 hours boiling) (ASTM C413) |
| Gloss Level | ~90 (60 degrees) (ASTM D523) |
| Mixing Ratio | A:B = 2:1 (by volume) |
| Product Temperature | Precondition material for at least 24 hours between 18 °C to 30 °C (65 °F to 86 °F) before using and during the application. |
| Ambient Air Temperature | Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F) Note: Mixing carried out under conditions where the Sikafloor®-217 temperature and ambient temperature are below 18°C (65°F) will result in reduced product workability and slower curing rates. |
| Relative Air Humidity | Maximum 85 % (during application and curing) |
| Dew Point | Substrate must be at least 3 °C (5 °F) above the Dew Point to reduce the risk of condensation, which may lead to adhesion failure or "blushing" on the floor finish. Be aware that the substrate temperature may be lower than the ambient temperature. |
| Substrate Temperature | Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F) Note: Any attempt to apply Sikafloor®-217 at substrate temperature conditions less than 18 °C (65 °F) will result in an increase in viscosity and slower cure rates. |
| Substrate Moisture Content | Moisture content of concrete substrate must be ≤ 4 % by mass (pbw – part by weight) as measured with a Tramex®CME / CMExpert type concrete moisture meter on mechanically prepared surface according to this product data sheet (preparation to ICRI / CSP 3 - 4). |
| Pot Life | Material Temperature Time 10 °C (50 °F) ~50 minutes 20 °C (68 °F) ~25 minutes 30 °C (86 °F) ~15 minutes |
| Curing Time | Temperature Foot Traffic Light Traffic Full Cure 10 °C (50 °F) ~24 hours ~3 days ~10 days 20 °C (68 °F) ~8 hours ~2 days ~7 days 30 °C (86 °F) ~6 hours ~36 hours ~4 days Curing times will vary according to air and substrate temperature and relative humidity. Protect from dampness, condensation and water contact during the initial 72 hour cure period. Mechanical, chemical and physical properties will be fully achieved at full cure. |
| Consumption | 2 m 2 /L to 4 m 2 /L (80 ft 2 / US gal to 160 ft 2 / US gal) at 10 - 20 mils w.f.t. |
| SUBSTRATE QUALITY | Concrete surfaces must be clean and sound. The compressive strength of the concrete substrate should be at least 25 MPa (3625 psi) at 28 days and a minimum of 1.5 MPa (217 psi) in tensile strength, at the time of the application. Substrates must be free of contaminants such as dust, dirt, existing paint films, efflorescence, exudates, laitance, form, hydraulic or fuel oils, brake fluid, grease, fungi, mildew, biological residues or any other contaminants which may prohibit good bond or conditions of the substrate that may reduce the overall performances of Sikafloor®-217. |
| APPLICATION | Apply Sikafloor®-217 using a non-marking squeegee or flexible steel trowel, followed by backrolling to provide a uniform texture and appearance. Over-rolling and or late back rolling may cause bubbling and leave roller marks. A second top coat application or a thicker initial application maybe required to achieve a specific texture or desired final appearance. Note: Sika Canada strongly recommends that a test area be applied to confirm specific top coat selection and application rates required to produce the desired final appearance. |
| CLEAN UP | Clean all tools and equipment with a non-flammable solvent. Once hardened, product can only be removed mechanically. |
| Cure time | Temperature Foot Traffic Light Traffic Full Cure 10 °C (50 °F) ~24 hours ~3 days ~10 days 20 °C (68 °F) ~8 hours ~2 days ~7 days 30 °C (86 °F) ~6 hours ~36 hours ~4 days Curing times will vary according to air and substrate temperature and relative humidity. |
| Application temperature | Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F) |
| VOC | ~56 g/L |
KNOW BEFORE
YOU COAT.
Technical information.
Safety information.
Ready when you need it.
Sikafloor®-217
Product Data Sheet (PDS) · Sikafloor®-217
Read the full product requirements, application instructions and limitations.
Safety Data Sheet (SDS) · SDS Sikafloor®-217 Part A
Product safety and handling information.
Safety Data Sheet (SDS) · SDS Sikafloor®-217 Part B
Product safety and handling information.
Safety Data Sheet (SDS) · SDS Sikafloor®-217/Sikagard®-215 Part B
Product safety and handling information.
Check the product label and current manufacturer documents for the exact component, colour and region before use.
Full product details, applications & manufacturer specifications
Sikafloor®-217 is a 100 % solids, low VOC, low odour, water-clear, aesthetic, high gloss epoxy resin used to create premium quality high build coatings, broadcast or trowel-applied surfacings such as Sikafloor® Quartzite®, DecoFlake®.
Sikafloor®-217 formulation contains raw materials and additives with approved performances blended to provide enhanced resistance to ultra violet light colour change over time.
Recommended uses
Sikafloor®-217 should only be used by qualified and experienced installers. Sikafloor®-217 provides an additional measure of long term colour stability in traditional interior seamless flooring installations that include: Laboratories, life sciences, pharmaceutical and health care Education (e.g., schools and universities) Leisure & culture (e.g., museums, stadiums) Retail spaces (grocery, department and retail stores) Bank, offices and government buildings Animal shelters and veterinary clinics Bathroom and shower areas
Floors- Finish
~90 (60 degrees) (ASTM D523)
- Coverage
2 m 2 /L to 4 m 2 /L (80 ft 2 / US gal to 160 ft 2 / US gal) at 10 - 20 mils w.f.t.
- Application method
Apply Sikafloor®-217 using a non-marking squeegee or flexible steel trowel, followed by backrolling to provide a uniform texture and appearance. Over-rolling and or late back rolling may cause bubbling and leave roller marks. A second top coat application or a thicker initial application maybe required to achieve a specific texture or desired final appearance. Note: Sika Canada strongly recommends that a test area be applied to confirm specific top coat selection and application rates required to produce the desired final appearance.
- Drying time
Curing Time: Temperature Foot Traffic Light Traffic Full Cure 10 °C (50 °F) ~24 hours ~3 days ~10 days 20 °C (68 °F) ~8 hours ~2 days ~7 days 30 °C (86 °F) ~6 hours ~36 hours ~4 days Curing times will vary according to air and substrate temperature and relative humidity. Protect from dampness, condensation and water contact during the initial 72 hour cure period. Mechanical, chemical and physical properties will be fully achieved at full cure.
- Recoat time
Temperature Minimum Maximum 10 °C (50 °F) ~24 hours 36 hours 20 °C (68 °F) ~8 hours 24 hours 30 °C (86 °F) ~6 hours 24 hours
Use the sheet for your exact product code and finish. Coverage and times depend on the stated temperature, humidity, substrate and coat thickness.
Features
- Enhanced resistance to long term UV light colour change
- 100 % solids as supplied
- Superior aesthetic glossy finish
- Durable, impermeable and seamless surface that is easy to clean
- Excellent impact resistance
- Easy cleaned and maintained
- Low VOC-content
- Packaging
- A+B = 10 L (2.64 US gal) Unit Component A: 6.67 L (1.76 US gal) Component B: 3.33 L (0.88 US gal)
- ENVIRONMENTAL INFORMATION
- Conformity with LEED® v4 MRc 2 (Option 1): Building Product Disclosure and Optimization – Environmental Product Declarations. Conformity with LEED® v4 EQc 2: Low-Emitting Materials.
- APPROVALS / CERTIFICATES
- Meets CFIA requirements for use in food plants.
- Shelf Life
- 2 years when stored in original, unopened packaging.
- Storage Conditions
- Store dry at temperatures between 5 °C to 32 °C (41 °F to 89 °F). Protect from freezing. If frozen, contact Sika Canada.
- Volatile organic compound (VOC) content
- ~56 g/L
- Viscosity
- A+B: ~500 cPs
- Solid content by volume
- ~100 %
- Shore D Hardness
- ~80 (ASTM D2240)
- Abrasion Resistance
- ~0,076 g loss: CS-17 wheel /1000 g /1000 cycles- (ASTM D4060)
- Compressive Strength
- ~49.9 MPa (~7250 psi) (ASTM C579)
- Tensile Strength
- ~39.5 MPa (~5728 psi) (ASTM D638)
- Pull-Off Strength
- > 2.5 MPa (> 363 psi) concrete failure (ASTM D7234)
- Chemical Resistance
- Consult Sika Canada
- Coefficient of Friction
- ~0.32 Wet (smooth coating) ~0.92 Dry (smooth coating) ANSI A326.3 (DCOF - BOT 3000e)
- Water Absorption
- ~0.13 % (2 hours boiling) (ASTM C413)
- Gloss Level
- ~90 (60 degrees) (ASTM D523)
- Mixing Ratio
- A:B = 2:1 (by volume)
- Product Temperature
- Precondition material for at least 24 hours between 18 °C to 30 °C (65 °F to 86 °F) before using and during the application.
- Ambient Air Temperature
- Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F) Note: Mixing carried out under conditions where the Sikafloor®-217 temperature and ambient temperature are below 18°C (65°F) will result in reduced product workability and slower curing rates.
- Relative Air Humidity
- Maximum 85 % (during application and curing)
- Dew Point
- Substrate must be at least 3 °C (5 °F) above the Dew Point to reduce the risk of condensation, which may lead to adhesion failure or "blushing" on the floor finish. Be aware that the substrate temperature may be lower than the ambient temperature.
- Substrate Temperature
- Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F) Note: Any attempt to apply Sikafloor®-217 at substrate temperature conditions less than 18 °C (65 °F) will result in an increase in viscosity and slower cure rates.
- Substrate Moisture Content
- Moisture content of concrete substrate must be ≤ 4 % by mass (pbw – part by weight) as measured with a Tramex®CME / CMExpert type concrete moisture meter on mechanically prepared surface according to this product data sheet (preparation to ICRI / CSP 3 - 4).
- Pot Life
- Material Temperature Time 10 °C (50 °F) ~50 minutes 20 °C (68 °F) ~25 minutes 30 °C (86 °F) ~15 minutes
- Curing Time
- Temperature Foot Traffic Light Traffic Full Cure 10 °C (50 °F) ~24 hours ~3 days ~10 days 20 °C (68 °F) ~8 hours ~2 days ~7 days 30 °C (86 °F) ~6 hours ~36 hours ~4 days Curing times will vary according to air and substrate temperature and relative humidity. Protect from dampness, condensation and water contact during the initial 72 hour cure period. Mechanical, chemical and physical properties will be fully achieved at full cure.
- Consumption
- 2 m 2 /L to 4 m 2 /L (80 ft 2 / US gal to 160 ft 2 / US gal) at 10 - 20 mils w.f.t.
- SUBSTRATE QUALITY
- Concrete surfaces must be clean and sound. The compressive strength of the concrete substrate should be at least 25 MPa (3625 psi) at 28 days and a minimum of 1.5 MPa (217 psi) in tensile strength, at the time of the application. Substrates must be free of contaminants such as dust, dirt, existing paint films, efflorescence, exudates, laitance, form, hydraulic or fuel oils, brake fluid, grease, fungi, mildew, biological residues or any other contaminants which may prohibit good bond or conditions of the substrate that may reduce the overall performances of Sikafloor®-217.
- APPLICATION
- Apply Sikafloor®-217 using a non-marking squeegee or flexible steel trowel, followed by backrolling to provide a uniform texture and appearance. Over-rolling and or late back rolling may cause bubbling and leave roller marks. A second top coat application or a thicker initial application maybe required to achieve a specific texture or desired final appearance. Note: Sika Canada strongly recommends that a test area be applied to confirm specific top coat selection and application rates required to produce the desired final appearance.
- CLEAN UP
- Clean all tools and equipment with a non-flammable solvent. Once hardened, product can only be removed mechanically.
- Cure time
- Temperature Foot Traffic Light Traffic Full Cure 10 °C (50 °F) ~24 hours ~3 days ~10 days 20 °C (68 °F) ~8 hours ~2 days ~7 days 30 °C (86 °F) ~6 hours ~36 hours ~4 days Curing times will vary according to air and substrate temperature and relative humidity.
- Application temperature
- Minimum: 10 °C (50 °F) / Maximum: 30 °C (86 °F)
- VOC
- ~56 g/L
Colours &
finish options.
Explore the published colour and finish information for this product.
Water-Clear / Pigmented with Sikafloor® Epoxy Pigment Pack CA
Sikafloor®-217 colour options
Water-clear resin or field-pigmented using the specified Sikafloor Epoxy Pigment Pack CA. Confirm the current product, pigment dosage and formula before use.
- Water-clear
Screen colours are approximate. Confirm your choice with a physical sample. Wood species, fabric opacity, preparation and the coating system can affect the result.
Complete your project.
Companion products for the selected product and system.
Sikafloor®-1620
A listed moisture-mitigation primer when the concrete requires it.
Conditional system option: the Sikafloor-217 sheet names Sikafloor-1620 when the measured concrete moisture exceeds its 4% limit. Follow the full Sika moisture test, concrete preparation and primer application requirements; obtain Sika recommendations for conditions outside the listed system.
Sikafloor®-315 N
An optional listed topcoat to help delay UV colour change.
Use only within the specified Sikafloor system and recoat windows. Sika notes that a UV-resistant topcoat can delay colour change but may not prevent discolouration of the underlying material. Confirm the desired texture and application rate with a test area.
Explore related categories
BIG PROJECT?
LET’S TALK.
Share the surface, its condition and what it needs to stand up to. We’ll help you work through the product choices and preparation.
Ask about Sikafloor®-217